40mm x 15mm Heavy Duty Aluminium Flat Bar


Price:
Sale price£76.72

Our Clients

Description

The 40mm x 15mm Aluminium Flat Bar is a premium, durable solution for both industrial and DIY applications. Crafted from high-quality aluminium, this flat bar offers exceptional strength, corrosion resistance, and versatility. The 15mm thickness makes it perfect for heavy-duty use in construction, fabrication, and engineering projects.

Lightweight yet sturdy, this aluminium flat bar is easy to cut, weld, and shape, making it suitable for a range of applications such as supports, frames, brackets, and more. Its smooth, polished surface ensures a professional finish, ideal for projects where aesthetics and functionality are important.

Key Features:

  • Dimensions: 40mm wide x 15mm thick
  • Material: High-quality aluminium for excellent durability and corrosion resistance
  • Ideal for Heavy-Duty Applications: Suitable for construction, fabrication, and engineering
  • Easy to Work With: Lightweight, easy to cut, weld, and shape
  • Multi-Purpose Use: Perfect for structural supports, brackets, and DIY projects

Specifications:

Grade 6082T6
Weight - Kg/m 1.62
Measurement Type Metric
Metric Size 40 mm x 15 mm
Finish Standard Mill Finish
Thickness 15 mm
Proof Stress 260 Min MPa
Tensile Strength 210 MPa
Elongation 8 Min %
Density 2.70 g/cm³
Melting Point 555 °C
Thermal Expansion 24 x10^-6 /K
Modulus of Elasticity 70 GPa
Thermal Conductivity 180 W/m.K
Electrical Resistivity 0.038 x10^-6 Ω .m
Machinability Good
Workability - Cold Good
Weldability - Gas Good
Weldability - Arc Good
Weldability - Resistance Good
Brazeability Good

About Us

Suppliers to Ministry of Defence, NATO, US Airforce and Most UK Councils, Schools, Universities, Hospitals & various Government departments

Payment & Security

American Express Apple Pay Diners Club Discover Google Pay Klarna Maestro Mastercard Shop Pay Union Pay Visa

Your payment information is processed securely. We do not store credit card details nor have access to your credit card information.

You may also like